High quality Phos Copper Welding Wires BAg10CuZn

High quality Phos Copper Welding Wires BAg10CuZn

Products Description Brazing    AlloyComposition(%)Melting    Range(℃)Applicable    scopeAgCuZnSnMinMax HL301 (as:BAg10CuZn)10.0±1.053±1.0REM 815850The    me...

Chat Now
Product Details

Products Description

Brazing    Alloy

Composition(%)

Melting    Range(℃)

Applicable    scope

Ag

Cu

Zn

Sn

Min

Max

 

HL301 (as:BAg10CuZn)

10.0±1.0

53±1.0

REM

 

815

850

The    melting point is high, the sheet flood attachment plasticity is bad,is mainly    suitable for the steel hard alloy copper, the copper alloy.

Comments


     Name:welding

Time:2012-12-11

Message
     Stainless steel    wire is what ingredients

Replay:
     1, martensitic stainless    steel electrode martensitic stainless steel, including 5 to 9% chromium in    chrome steel and chromium 12% of high-chromium steel. Such steel hardened    tendency, after welding, is easy to produce a high hardness martensite and    bainite so that brittleness increases, the residual stress is also large,    easy to produce cold cracks. Must be so general before welding preheat and    inter-layer insulation, high-temperature tempering after welding yet cooled.    2, chrome 13 stainless steel welding: these chrome steel after welding    sclerosing easily cracks, the use of a similar chromium stainless steel electrode    (CHK202, CHK207) welding, preheat and solder must be above 300 ℃ 700 ℃ and tempering slow cooling process. If the    weldments can not weld treatment, the application of a chromium stainless    steel electrode welding (CHS107, CHS207). 3, Chromium 17 stainless steel    welding: Such chromium steel usually improving the corrosion resistance and    weldability and add the appropriate amount of the stabilizing elements    titanium, niobium, molybdenum, weldability than chromium 13 steel as well,    the same type can be used chromium stainless steel welding electrodes    (CHK302, CHK307). Before welding, weldment should be about 200 ℃ preheat about 800 ℃ tempering after welding. Can also be    used chrome-nickel stainless steel electrode (such CHS107 CHS207), post-weld    heat treatment.

Hot Tags: High quality Phos Copper Welding Wires BAg10CuZn, Phos Copper Welding Wires
Related Products
Inquiry